S44800 Stainless Steel vs. Solder Alloy 113

S44800 stainless steel belongs to the iron alloys classification, while solder alloy 113 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S44800 stainless steel and the bottom bar is solder alloy 113.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
32
Elongation at Break, % 23
32
Poisson's Ratio 0.27
0.4
Shear Modulus, GPa 82
11
Tensile Strength: Ultimate (UTS), MPa 590
39

Thermal Properties

Latent Heat of Fusion, J/g 300
40
Melting Completion (Liquidus), °C 1460
230
Melting Onset (Solidus), °C 1410
180
Specific Heat Capacity, J/kg-K 480
170
Thermal Conductivity, W/m-K 17
46
Thermal Expansion, µm/m-K 11
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.6
10
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
9.8

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.5
Embodied Carbon, kg CO2/kg material 3.8
8.9
Embodied Energy, MJ/kg 52
150
Embodied Water, L/kg 190
800

Common Calculations

Stiffness to Weight: Axial, points 15
1.8
Stiffness to Weight: Bending, points 25
11
Strength to Weight: Axial, points 21
1.1
Strength to Weight: Bending, points 20
2.7
Thermal Diffusivity, mm2/s 4.6
28
Thermal Shock Resistance, points 19
3.4

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 28 to 30
0
Copper (Cu), % 0 to 0.15
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 62.6 to 66.5
0 to 0.020
Lead (Pb), % 0
53.4 to 55.5
Manganese (Mn), % 0 to 0.3
0
Molybdenum (Mo), % 3.5 to 4.2
0
Nickel (Ni), % 2.0 to 2.5
0 to 0.010
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.2
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
44.5 to 45.5
Zinc (Zn), % 0
0 to 0.0010