S44800 Stainless Steel vs. Solder Alloy 114

S44800 stainless steel belongs to the iron alloys classification, while solder alloy 114 belongs to the otherwise unclassified metals. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S44800 stainless steel and the bottom bar is solder alloy 114.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
12
Elastic (Young's, Tensile) Modulus, GPa 210
30
Elongation at Break, % 23
25
Poisson's Ratio 0.27
0.41
Shear Modulus, GPa 82
11
Tensile Strength: Ultimate (UTS), MPa 590
37

Thermal Properties

Latent Heat of Fusion, J/g 300
38
Melting Completion (Liquidus), °C 1460
240
Melting Onset (Solidus), °C 1410
180
Specific Heat Capacity, J/kg-K 480
170
Thermal Conductivity, W/m-K 17
44
Thermal Expansion, µm/m-K 11
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.6
10
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
95
Density, g/cm3 7.8
9.7
Embodied Carbon, kg CO2/kg material 3.8
8.3
Embodied Energy, MJ/kg 52
140
Embodied Water, L/kg 190
760

Common Calculations

Stiffness to Weight: Axial, points 15
1.7
Stiffness to Weight: Bending, points 25
11
Strength to Weight: Axial, points 21
1.1
Strength to Weight: Bending, points 20
2.6
Thermal Diffusivity, mm2/s 4.6
27
Thermal Shock Resistance, points 19
3.4

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 28 to 30
0
Copper (Cu), % 0 to 0.15
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 62.6 to 66.5
0 to 0.020
Lead (Pb), % 0
58.4 to 60.5
Manganese (Mn), % 0 to 0.3
0
Molybdenum (Mo), % 3.5 to 4.2
0
Nickel (Ni), % 2.0 to 2.5
0 to 0.010
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.2
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
39.5 to 40.5
Zinc (Zn), % 0
0 to 0.0010