S44800 Stainless Steel vs. Solder Alloy 133

S44800 stainless steel belongs to the iron alloys classification, while solder alloy 133 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S44800 stainless steel and the bottom bar is solder alloy 133.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
33
Elongation at Break, % 23
34
Poisson's Ratio 0.27
0.4
Shear Modulus, GPa 82
12
Tensile Strength: Ultimate (UTS), MPa 590
41

Thermal Properties

Latent Heat of Fusion, J/g 300
42
Melting Completion (Liquidus), °C 1460
220
Melting Onset (Solidus), °C 1410
180
Specific Heat Capacity, J/kg-K 480
180
Thermal Conductivity, W/m-K 17
47
Thermal Expansion, µm/m-K 11
25

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.6
11
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
10

Otherwise Unclassified Properties

Density, g/cm3 7.8
9.3
Embodied Carbon, kg CO2/kg material 3.8
9.4
Embodied Energy, MJ/kg 52
160
Embodied Water, L/kg 190
840

Common Calculations

Stiffness to Weight: Axial, points 15
2.0
Stiffness to Weight: Bending, points 25
12
Strength to Weight: Axial, points 21
1.2
Strength to Weight: Bending, points 20
2.9
Thermal Diffusivity, mm2/s 4.6
29
Thermal Shock Resistance, points 19
3.5

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0.2 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.010
0
Chromium (Cr), % 28 to 30
0
Copper (Cu), % 0 to 0.15
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 62.6 to 66.5
0 to 0.020
Lead (Pb), % 0
48.5 to 50.3
Manganese (Mn), % 0 to 0.3
0
Molybdenum (Mo), % 3.5 to 4.2
0
Nickel (Ni), % 2.0 to 2.5
0 to 0.010
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.2
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.020
0
Tin (Sn), % 0
49.5 to 50.5
Zinc (Zn), % 0
0 to 0.0010