S64512 Stainless Steel vs. ASTM A369 Grade FP11

Both S64512 stainless steel and ASTM A369 grade FP11 are iron alloys. They have 85% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is ASTM A369 grade FP11.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
20
Fatigue Strength, MPa 540
160
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 700
300
Tensile Strength: Ultimate (UTS), MPa 1140
470
Tensile Strength: Yield (Proof), MPa 890
240

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Maximum Temperature: Mechanical, °C 750
430
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 28
40
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.3
1.6
Embodied Energy, MJ/kg 47
21
Embodied Water, L/kg 110
52

Common Calculations

PREN (Pitting Resistance) 18
3.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
80
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
150
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 40
17
Strength to Weight: Bending, points 31
17
Thermal Diffusivity, mm2/s 7.5
11
Thermal Shock Resistance, points 42
14

Alloy Composition

Carbon (C), % 0.080 to 0.15
0.050 to 0.15
Chromium (Cr), % 11 to 12.5
1.0 to 1.5
Iron (Fe), % 80.6 to 84.7
96.1 to 97.7
Manganese (Mn), % 0.5 to 0.9
0.3 to 0.6
Molybdenum (Mo), % 1.5 to 2.0
0.44 to 0.65
Nickel (Ni), % 2.0 to 3.0
0
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.35
0.5 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.025
Vanadium (V), % 0.25 to 0.4
0