S64512 Stainless Steel vs. AWS BCo-1

S64512 stainless steel belongs to the iron alloys classification, while AWS BCo-1 belongs to the cobalt alloys. There are 18 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is AWS BCo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 76
78
Tensile Strength: Ultimate (UTS), MPa 1140
700

Thermal Properties

Latent Heat of Fusion, J/g 270
420
Melting Completion (Liquidus), °C 1460
1150
Melting Onset (Solidus), °C 1420
1120
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.3
8.0
Embodied Energy, MJ/kg 47
110
Embodied Water, L/kg 110
430

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 40
24
Strength to Weight: Bending, points 31
22
Thermal Shock Resistance, points 42
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0
0.7 to 0.9
Carbon (C), % 0.080 to 0.15
0.35 to 0.45
Chromium (Cr), % 11 to 12.5
18 to 20
Cobalt (Co), % 0
46 to 54
Iron (Fe), % 80.6 to 84.7
0 to 1.0
Manganese (Mn), % 0.5 to 0.9
0
Molybdenum (Mo), % 1.5 to 2.0
0
Nickel (Ni), % 2.0 to 3.0
16 to 18
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 0.35
7.5 to 8.5
Sulfur (S), % 0 to 0.025
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Tungsten (W), % 0
3.5 to 4.5
Vanadium (V), % 0.25 to 0.4
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5