S64512 Stainless Steel vs. AWS BNi-5

S64512 stainless steel belongs to the iron alloys classification, while AWS BNi-5 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is AWS BNi-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 1140
470

Thermal Properties

Latent Heat of Fusion, J/g 270
470
Melting Completion (Liquidus), °C 1460
1140
Melting Onset (Solidus), °C 1420
1080
Specific Heat Capacity, J/kg-K 470
510
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Base Metal Price, % relative 10
55
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.3
8.9
Embodied Energy, MJ/kg 47
130
Embodied Water, L/kg 110
260

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 40
17
Strength to Weight: Bending, points 31
17
Thermal Shock Resistance, points 42
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0
0 to 0.030
Carbon (C), % 0.080 to 0.15
0 to 0.060
Chromium (Cr), % 11 to 12.5
18.5 to 19.5
Cobalt (Co), % 0
0 to 0.1
Iron (Fe), % 80.6 to 84.7
0
Manganese (Mn), % 0.5 to 0.9
0
Molybdenum (Mo), % 1.5 to 2.0
0
Nickel (Ni), % 2.0 to 3.0
69.1 to 71.8
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0 to 0.35
9.8 to 10.5
Sulfur (S), % 0 to 0.025
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0.25 to 0.4
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5