S64512 Stainless Steel vs. AWS E309L

Both S64512 stainless steel and AWS E309L are iron alloys. They have 76% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is AWS E309L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
34
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 1140
580

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 28
15
Thermal Expansion, µm/m-K 10
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 10
20
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.3
3.7
Embodied Energy, MJ/kg 47
52
Embodied Water, L/kg 110
180

Common Calculations

PREN (Pitting Resistance) 18
25
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 40
21
Strength to Weight: Bending, points 31
20
Thermal Diffusivity, mm2/s 7.5
4.0
Thermal Shock Resistance, points 42
15

Alloy Composition

Carbon (C), % 0.080 to 0.15
0 to 0.040
Chromium (Cr), % 11 to 12.5
22 to 25
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 80.6 to 84.7
55.9 to 65.5
Manganese (Mn), % 0.5 to 0.9
0.5 to 2.5
Molybdenum (Mo), % 1.5 to 2.0
0 to 0.75
Nickel (Ni), % 2.0 to 3.0
12 to 14
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Vanadium (V), % 0.25 to 0.4
0