S64512 Stainless Steel vs. AWS ERNiMo-3

S64512 stainless steel belongs to the iron alloys classification, while AWS ERNiMo-3 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is AWS ERNiMo-3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 76
83
Tensile Strength: Ultimate (UTS), MPa 1140
770

Thermal Properties

Latent Heat of Fusion, J/g 270
320
Melting Completion (Liquidus), °C 1460
1600
Melting Onset (Solidus), °C 1420
1540
Specific Heat Capacity, J/kg-K 470
400
Thermal Expansion, µm/m-K 10
11

Otherwise Unclassified Properties

Base Metal Price, % relative 10
70
Density, g/cm3 7.8
9.1
Embodied Carbon, kg CO2/kg material 3.3
15
Embodied Energy, MJ/kg 47
190
Embodied Water, L/kg 110
270

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 40
24
Strength to Weight: Bending, points 31
21
Thermal Shock Resistance, points 42
24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.080 to 0.15
0 to 0.12
Chromium (Cr), % 11 to 12.5
4.0 to 6.0
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 80.6 to 84.7
4.0 to 7.0
Manganese (Mn), % 0.5 to 0.9
0 to 1.0
Molybdenum (Mo), % 1.5 to 2.0
23 to 26
Nickel (Ni), % 2.0 to 3.0
53.7 to 69
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
0 to 1.0
Vanadium (V), % 0.25 to 0.4
0 to 0.6
Residuals, % 0
0 to 0.5