S64512 Stainless Steel vs. EN 1.0236 Steel

Both S64512 stainless steel and EN 1.0236 steel are iron alloys. They have 84% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is EN 1.0236 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
23
Fatigue Strength, MPa 540
230
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 700
310
Tensile Strength: Ultimate (UTS), MPa 1140
490
Tensile Strength: Yield (Proof), MPa 890
330

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 750
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 28
52
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 10
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.3
1.4
Embodied Energy, MJ/kg 47
18
Embodied Water, L/kg 110
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
99
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
290
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 40
17
Strength to Weight: Bending, points 31
18
Thermal Diffusivity, mm2/s 7.5
14
Thermal Shock Resistance, points 42
16

Alloy Composition

Carbon (C), % 0.080 to 0.15
0 to 0.21
Chromium (Cr), % 11 to 12.5
0
Iron (Fe), % 80.6 to 84.7
97.9 to 100
Manganese (Mn), % 0.5 to 0.9
0 to 1.5
Molybdenum (Mo), % 1.5 to 2.0
0
Nickel (Ni), % 2.0 to 3.0
0
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.35
0 to 0.3
Sulfur (S), % 0 to 0.025
0 to 0.035
Vanadium (V), % 0.25 to 0.4
0