S64512 Stainless Steel vs. EN 1.4563 Stainless Steel

Both S64512 stainless steel and EN 1.4563 stainless steel are iron alloys. They have 53% of their average alloy composition in common. There are 34 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is EN 1.4563 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
200
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
40
Fatigue Strength, MPa 540
210
Impact Strength: V-Notched Charpy, J 47
91
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
80
Shear Strength, MPa 700
420
Tensile Strength: Ultimate (UTS), MPa 1140
620
Tensile Strength: Yield (Proof), MPa 890
250

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Maximum Temperature: Corrosion, °C 390
460
Maximum Temperature: Mechanical, °C 750
1100
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 28
12
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 10
36
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.3
6.3
Embodied Energy, MJ/kg 47
87
Embodied Water, L/kg 110
240

Common Calculations

PREN (Pitting Resistance) 18
39
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
200
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 40
21
Strength to Weight: Bending, points 31
20
Thermal Diffusivity, mm2/s 7.5
3.2
Thermal Shock Resistance, points 42
13

Alloy Composition

Carbon (C), % 0.080 to 0.15
0 to 0.020
Chromium (Cr), % 11 to 12.5
26 to 28
Copper (Cu), % 0
0.7 to 1.5
Iron (Fe), % 80.6 to 84.7
31.6 to 40.3
Manganese (Mn), % 0.5 to 0.9
0 to 2.0
Molybdenum (Mo), % 1.5 to 2.0
3.0 to 4.0
Nickel (Ni), % 2.0 to 3.0
30 to 32
Nitrogen (N), % 0.010 to 0.050
0 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.35
0 to 0.7
Sulfur (S), % 0 to 0.025
0 to 0.010
Vanadium (V), % 0.25 to 0.4
0