S64512 Stainless Steel vs. EN 1.4600 Stainless Steel

Both S64512 stainless steel and EN 1.4600 stainless steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is EN 1.4600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
23
Fatigue Strength, MPa 540
290
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 700
360
Tensile Strength: Ultimate (UTS), MPa 1140
580
Tensile Strength: Yield (Proof), MPa 890
430

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Corrosion, °C 390
420
Maximum Temperature: Mechanical, °C 750
730
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 28
27
Thermal Expansion, µm/m-K 10
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 10
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.3
2.0
Embodied Energy, MJ/kg 47
28
Embodied Water, L/kg 110
100

Common Calculations

PREN (Pitting Resistance) 18
12
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
120
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
470
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 40
21
Strength to Weight: Bending, points 31
20
Thermal Diffusivity, mm2/s 7.5
7.3
Thermal Shock Resistance, points 42
21

Alloy Composition

Carbon (C), % 0.080 to 0.15
0 to 0.030
Chromium (Cr), % 11 to 12.5
11 to 13
Iron (Fe), % 80.6 to 84.7
82 to 87.7
Manganese (Mn), % 0.5 to 0.9
1.0 to 2.5
Molybdenum (Mo), % 1.5 to 2.0
0
Nickel (Ni), % 2.0 to 3.0
0.3 to 1.0
Nitrogen (N), % 0.010 to 0.050
0 to 0.025
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Titanium (Ti), % 0
0 to 0.35
Vanadium (V), % 0.25 to 0.4
0