S64512 Stainless Steel vs. EN 1.5113 Steel

Both S64512 stainless steel and EN 1.5113 steel are iron alloys. They have 84% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is EN 1.5113 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
170 to 270
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
11 to 18
Fatigue Strength, MPa 540
220 to 470
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Shear Strength, MPa 700
360 to 540
Tensile Strength: Ultimate (UTS), MPa 1140
580 to 900
Tensile Strength: Yield (Proof), MPa 890
320 to 770

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Maximum Temperature: Mechanical, °C 750
400
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 28
52
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.3
1.4
Embodied Energy, MJ/kg 47
19
Embodied Water, L/kg 110
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
91 to 96
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
270 to 1570
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 40
21 to 32
Strength to Weight: Bending, points 31
20 to 27
Thermal Diffusivity, mm2/s 7.5
14
Thermal Shock Resistance, points 42
17 to 26

Alloy Composition

Carbon (C), % 0.080 to 0.15
0 to 0.1
Chromium (Cr), % 11 to 12.5
0
Iron (Fe), % 80.6 to 84.7
97 to 97.5
Manganese (Mn), % 0.5 to 0.9
1.6 to 1.8
Molybdenum (Mo), % 1.5 to 2.0
0
Nickel (Ni), % 2.0 to 3.0
0
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.35
0.9 to 1.1
Sulfur (S), % 0 to 0.025
0 to 0.025
Vanadium (V), % 0.25 to 0.4
0