S64512 Stainless Steel vs. EN 1.7149 Steel

Both S64512 stainless steel and EN 1.7149 steel are iron alloys. They have 85% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is EN 1.7149 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 1140
500 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 750
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 28
46
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.3
1.5
Embodied Energy, MJ/kg 47
19
Embodied Water, L/kg 110
52

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 40
18 to 52
Strength to Weight: Bending, points 31
18 to 36
Thermal Diffusivity, mm2/s 7.5
12
Thermal Shock Resistance, points 42
15 to 42

Alloy Composition

Carbon (C), % 0.080 to 0.15
0.17 to 0.22
Chromium (Cr), % 11 to 12.5
1.0 to 1.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 80.6 to 84.7
96.5 to 97.7
Manganese (Mn), % 0.5 to 0.9
1.1 to 1.4
Molybdenum (Mo), % 1.5 to 2.0
0
Nickel (Ni), % 2.0 to 3.0
0
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.35
0 to 0.3
Sulfur (S), % 0 to 0.025
0.020 to 0.040
Vanadium (V), % 0.25 to 0.4
0