S64512 Stainless Steel vs. EN 1.7366 Steel

Both S64512 stainless steel and EN 1.7366 steel are iron alloys. They have 89% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is EN 1.7366 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
140 to 210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
17 to 19
Fatigue Strength, MPa 540
160 to 320
Impact Strength: V-Notched Charpy, J 47
38
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
74
Shear Strength, MPa 700
290 to 440
Tensile Strength: Ultimate (UTS), MPa 1140
460 to 710
Tensile Strength: Yield (Proof), MPa 890
230 to 480

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Maximum Temperature: Mechanical, °C 750
510
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 28
40
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
9.3

Otherwise Unclassified Properties

Base Metal Price, % relative 10
4.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.3
1.7
Embodied Energy, MJ/kg 47
23
Embodied Water, L/kg 110
69

Common Calculations

PREN (Pitting Resistance) 18
6.8
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
74 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
140 to 600
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 40
16 to 25
Strength to Weight: Bending, points 31
17 to 23
Thermal Diffusivity, mm2/s 7.5
11
Thermal Shock Resistance, points 42
13 to 20

Alloy Composition

Carbon (C), % 0.080 to 0.15
0 to 0.18
Chromium (Cr), % 11 to 12.5
4.0 to 6.0
Iron (Fe), % 80.6 to 84.7
91.9 to 95.3
Manganese (Mn), % 0.5 to 0.9
0.3 to 0.8
Molybdenum (Mo), % 1.5 to 2.0
0.45 to 0.65
Nickel (Ni), % 2.0 to 3.0
0
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.015
Vanadium (V), % 0.25 to 0.4
0