S64512 Stainless Steel vs. EN 1.8062 Steel

Both S64512 stainless steel and EN 1.8062 steel are iron alloys. They have 85% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is EN 1.8062 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
200 to 510
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 1140
660 to 1910

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Mechanical, °C 750
420
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 28
43
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.4
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.3
1.5
Embodied Energy, MJ/kg 47
20
Embodied Water, L/kg 110
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 40
24 to 69
Strength to Weight: Bending, points 31
22 to 44
Thermal Diffusivity, mm2/s 7.5
12
Thermal Shock Resistance, points 42
20 to 57

Alloy Composition

Carbon (C), % 0.080 to 0.15
0.42 to 0.5
Chromium (Cr), % 11 to 12.5
0.5 to 0.8
Iron (Fe), % 80.6 to 84.7
95.9 to 97.1
Manganese (Mn), % 0.5 to 0.9
0.5 to 0.8
Molybdenum (Mo), % 1.5 to 2.0
0.2 to 0.3
Nickel (Ni), % 2.0 to 3.0
0
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.35
1.3 to 1.7
Sulfur (S), % 0 to 0.025
0 to 0.025
Vanadium (V), % 0.25 to 0.4
0