S64512 Stainless Steel vs. EN 1.8836 Steel

Both S64512 stainless steel and EN 1.8836 steel are iron alloys. They have 84% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is EN 1.8836 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
21
Fatigue Strength, MPa 540
290
Impact Strength: V-Notched Charpy, J 47
58
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 700
360
Tensile Strength: Ultimate (UTS), MPa 1140
570
Tensile Strength: Yield (Proof), MPa 890
410

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 750
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 28
44
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.3
1.7
Embodied Energy, MJ/kg 47
23
Embodied Water, L/kg 110
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
450
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 40
20
Strength to Weight: Bending, points 31
19
Thermal Diffusivity, mm2/s 7.5
12
Thermal Shock Resistance, points 42
17

Alloy Composition

Aluminum (Al), % 0
0.015 to 0.054
Carbon (C), % 0.080 to 0.15
0 to 0.18
Chromium (Cr), % 11 to 12.5
0 to 0.35
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 80.6 to 84.7
95.1 to 99.985
Manganese (Mn), % 0.5 to 0.9
0 to 1.8
Molybdenum (Mo), % 1.5 to 2.0
0 to 0.23
Nickel (Ni), % 2.0 to 3.0
0 to 0.85
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0.010 to 0.050
0 to 0.027
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.35
0 to 0.55
Sulfur (S), % 0 to 0.025
0 to 0.025
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0.25 to 0.4
0 to 0.14