S64512 Stainless Steel vs. EN 1.8874 Steel

Both S64512 stainless steel and EN 1.8874 steel are iron alloys. They have 85% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is EN 1.8874 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
19
Fatigue Strength, MPa 540
340
Impact Strength: V-Notched Charpy, J 47
68
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 700
410
Tensile Strength: Ultimate (UTS), MPa 1140
660
Tensile Strength: Yield (Proof), MPa 890
500

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 750
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 28
39
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 10
3.2
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.3
1.8
Embodied Energy, MJ/kg 47
24
Embodied Water, L/kg 110
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
120
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
670
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 40
23
Strength to Weight: Bending, points 31
21
Thermal Diffusivity, mm2/s 7.5
10
Thermal Shock Resistance, points 42
19

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0.080 to 0.15
0 to 0.18
Chromium (Cr), % 11 to 12.5
0 to 1.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 80.6 to 84.7
93.6 to 100
Manganese (Mn), % 0.5 to 0.9
0 to 1.7
Molybdenum (Mo), % 1.5 to 2.0
0 to 0.7
Nickel (Ni), % 2.0 to 3.0
0 to 1.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.010 to 0.050
0 to 0.015
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.35
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0.25 to 0.4
0 to 0.080
Zirconium (Zr), % 0
0 to 0.15