S64512 Stainless Steel vs. Monel R-405

S64512 stainless steel belongs to the iron alloys classification, while Monel R-405 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is Monel R-405.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
160
Elongation at Break, % 17
9.1 to 39
Fatigue Strength, MPa 540
210 to 250
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 76
62
Shear Strength, MPa 700
350 to 370
Tensile Strength: Ultimate (UTS), MPa 1140
540 to 630
Tensile Strength: Yield (Proof), MPa 890
190 to 350

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Mechanical, °C 750
900
Melting Completion (Liquidus), °C 1460
1350
Melting Onset (Solidus), °C 1420
1300
Specific Heat Capacity, J/kg-K 470
430
Thermal Conductivity, W/m-K 28
23
Thermal Expansion, µm/m-K 10
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
3.4
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 10
50
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 3.3
7.9
Embodied Energy, MJ/kg 47
110
Embodied Water, L/kg 110
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
49 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
120 to 370
Stiffness to Weight: Axial, points 14
10
Stiffness to Weight: Bending, points 25
21
Strength to Weight: Axial, points 40
17 to 20
Strength to Weight: Bending, points 31
17 to 18
Thermal Diffusivity, mm2/s 7.5
5.9
Thermal Shock Resistance, points 42
17 to 20

Alloy Composition

Carbon (C), % 0.080 to 0.15
0 to 0.3
Chromium (Cr), % 11 to 12.5
0
Copper (Cu), % 0
28 to 34
Iron (Fe), % 80.6 to 84.7
0 to 2.5
Manganese (Mn), % 0.5 to 0.9
0 to 2.0
Molybdenum (Mo), % 1.5 to 2.0
0
Nickel (Ni), % 2.0 to 3.0
63 to 72
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.35
0 to 0.5
Sulfur (S), % 0 to 0.025
0.025 to 0.060
Vanadium (V), % 0.25 to 0.4
0