S64512 Stainless Steel vs. N06002 Nickel

S64512 stainless steel belongs to the iron alloys classification, while N06002 nickel belongs to the nickel alloys. They have a modest 35% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is N06002 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 17
41
Fatigue Strength, MPa 540
250
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
81
Shear Strength, MPa 700
520
Tensile Strength: Ultimate (UTS), MPa 1140
760
Tensile Strength: Yield (Proof), MPa 890
310

Thermal Properties

Latent Heat of Fusion, J/g 270
320
Maximum Temperature: Mechanical, °C 750
990
Melting Completion (Liquidus), °C 1460
1360
Melting Onset (Solidus), °C 1420
1260
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 28
9.9
Thermal Expansion, µm/m-K 10
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 10
55
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 3.3
9.3
Embodied Energy, MJ/kg 47
130
Embodied Water, L/kg 110
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
250
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
230
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 40
25
Strength to Weight: Bending, points 31
22
Thermal Diffusivity, mm2/s 7.5
2.6
Thermal Shock Resistance, points 42
19

Alloy Composition

Carbon (C), % 0.080 to 0.15
0.050 to 0.15
Chromium (Cr), % 11 to 12.5
20.5 to 23
Cobalt (Co), % 0
0.5 to 2.5
Iron (Fe), % 80.6 to 84.7
17 to 20
Manganese (Mn), % 0.5 to 0.9
0 to 1.0
Molybdenum (Mo), % 1.5 to 2.0
8.0 to 10
Nickel (Ni), % 2.0 to 3.0
42.3 to 54
Nitrogen (N), % 0.010 to 0.050
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
0.2 to 1.0
Vanadium (V), % 0.25 to 0.4
0