S64512 Stainless Steel vs. S40977 Stainless Steel

Both S64512 stainless steel and S40977 stainless steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S64512 stainless steel and the bottom bar is S40977 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
21
Fatigue Strength, MPa 540
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 700
320
Tensile Strength: Ultimate (UTS), MPa 1140
510
Tensile Strength: Yield (Proof), MPa 890
310

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Corrosion, °C 390
390
Maximum Temperature: Mechanical, °C 750
720
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 28
25
Thermal Expansion, µm/m-K 10
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 4.1
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 10
6.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.3
1.9
Embodied Energy, MJ/kg 47
27
Embodied Water, L/kg 110
97

Common Calculations

PREN (Pitting Resistance) 18
12
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
92
Resilience: Unit (Modulus of Resilience), kJ/m3 2020
250
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 40
18
Strength to Weight: Bending, points 31
18
Thermal Diffusivity, mm2/s 7.5
6.7
Thermal Shock Resistance, points 42
18

Alloy Composition

Carbon (C), % 0.080 to 0.15
0 to 0.030
Chromium (Cr), % 11 to 12.5
10.5 to 12.5
Iron (Fe), % 80.6 to 84.7
83.9 to 89.2
Manganese (Mn), % 0.5 to 0.9
0 to 1.5
Molybdenum (Mo), % 1.5 to 2.0
0
Nickel (Ni), % 2.0 to 3.0
0.3 to 1.0
Nitrogen (N), % 0.010 to 0.050
0 to 0.030
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Vanadium (V), % 0.25 to 0.4
0