S82012 Stainless Steel vs. SAE-AISI 81B45 Steel

Both S82012 stainless steel and SAE-AISI 81B45 steel are iron alloys. They have 77% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S82012 stainless steel and the bottom bar is SAE-AISI 81B45 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
12 to 24
Fatigue Strength, MPa 480
250 to 350
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 550
340 to 400
Tensile Strength: Ultimate (UTS), MPa 800
540 to 670
Tensile Strength: Yield (Proof), MPa 560
350 to 560

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 950
410
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
40
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 11
2.3
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.4
1.5
Embodied Energy, MJ/kg 35
20
Embodied Water, L/kg 140
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 290
77 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 790
320 to 840
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 29
19 to 24
Strength to Weight: Bending, points 25
19 to 22
Thermal Diffusivity, mm2/s 3.9
11
Thermal Shock Resistance, points 23
17 to 21

Alloy Composition

Boron (B), % 0
0.00050 to 0.0030
Carbon (C), % 0 to 0.050
0.43 to 0.48
Chromium (Cr), % 19 to 20.5
0.35 to 0.55
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 71.3 to 77.9
97 to 98
Manganese (Mn), % 2.0 to 4.0
0.75 to 1.0
Molybdenum (Mo), % 0.1 to 0.6
0.080 to 0.15
Nickel (Ni), % 0.8 to 1.5
0.2 to 0.4
Nitrogen (N), % 0.16 to 0.26
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 0.8
0.15 to 0.35
Sulfur (S), % 0 to 0.0050
0 to 0.040