MakeItFrom.com
Menu (ESC)

Z21210 Zinc vs. R60802 Alloy

Z21210 zinc belongs to the zinc alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is Z21210 zinc and the bottom bar is R60802 alloy.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 7.1
6.5
Specific Heat Capacity, J/kg-K 400
270
Strength to Weight: Axial, points 5.7 to 6.4
18
Strength to Weight: Bending, points 8.6 to 9.4
19
Tensile Strength: Ultimate (UTS), MPa 150 to 170
430
Thermal Conductivity, W/m-K 110
22
Thermal Diffusivity, mm2/s 38
12
Thermal Expansion, µm/m-K 32
6.0