Z21210 Zinc vs. Z40101 Zinc
Both Z21210 zinc and Z40101 zinc are zinc alloys. There are 12 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is Z21210 zinc and the bottom bar is Z40101 zinc.
Metric UnitsUS Customary Units
|Tensile Strength: Ultimate (UTS), MPa||150 to 170|
|Melting Completion (Liquidus), °C||420|
|Melting Onset (Solidus), °C||420|
|Specific Heat Capacity, J/kg-K||400|
|Thermal Conductivity, W/m-K||110|
|Thermal Expansion, µm/m-K||32|
|Electrical Conductivity: Equal Volume, % IACS||28|
|Electrical Conductivity: Equal Weight (Specific), % IACS||35|
Otherwise Unclassified Properties
|Strength to Weight: Axial, points||5.7 to 6.4|
|Strength to Weight: Bending, points||8.6 to 9.4|
|Thermal Diffusivity, mm2/s||38|