UHMW-PE vs. UPVC
Both UHMW-PE and uPVC are thermoplastics. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is UHMW-PE and the bottom bar is uPVC.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 0.8 | |
| 3.7 |
| Elongation at Break, % | 400 | |
| 58 |
| Tensile Strength: Ultimate (UTS), MPa | 49 | |
| 47 |
Thermal Properties
| Melting Onset (Solidus), °C | 130 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 1750 | |
| 880 |
| Thermal Conductivity, W/m-K | 0.41 | |
| 0.16 |
| Thermal Expansion, µm/m-K | 180 | |
| 61 |
| Vicat Softening Temperature, °C | 75 | |
| 83 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 2.2 | |
| 3.4 |
| Electrical Dissipation At 1 Hz | 0.045 | |
| 0.013 |
Otherwise Unclassified Properties
| Density, g/cm3 | 0.94 | |
| 1.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.47 | |
| 1.5 |
| Stiffness to Weight: Bending, points | 33 | |
| 37 |
| Strength to Weight: Axial, points | 14 | |
| 9.1 |
| Strength to Weight: Bending, points | 32 | |
| 20 |
| Thermal Diffusivity, mm2/s | 0.25 | |
| 0.13 |
| Thermal Shock Resistance, points | 25 | |
| 15 |