WE43A Magnesium vs. S31727 Stainless Steel
WE43A magnesium belongs to the magnesium alloys classification, while S31727 stainless steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is WE43A magnesium and the bottom bar is S31727 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 200 |
| Elongation at Break, % | 5.2 to 5.4 | |
| 40 |
| Fatigue Strength, MPa | 85 to 120 | |
| 240 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 17 | |
| 78 |
| Shear Strength, MPa | 160 | |
| 430 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 270 | |
| 630 |
| Tensile Strength: Yield (Proof), MPa | 160 to 170 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 1010 |
| Melting Completion (Liquidus), °C | 640 | |
| 1440 |
| Melting Onset (Solidus), °C | 570 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 960 | |
| 470 |
| Thermal Expansion, µm/m-K | 27 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 24 |
| Density, g/cm3 | 1.9 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 28 | |
| 4.7 |
| Embodied Energy, MJ/kg | 250 | |
| 64 |
| Embodied Water, L/kg | 910 | |
| 180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 | |
| 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 310 | |
| 190 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 61 | |
| 24 |
| Strength to Weight: Axial, points | 36 to 39 | |
| 22 |
| Strength to Weight: Bending, points | 46 to 48 | |
| 20 |
| Thermal Shock Resistance, points | 15 to 16 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 17.5 to 19 |
| Copper (Cu), % | 0 to 0.030 | |
| 2.8 to 4.0 |
| Iron (Fe), % | 0 to 0.010 | |
| 53.7 to 61.3 |
| Lithium (Li), % | 0 to 0.2 | |
| 0 |
| Magnesium (Mg), % | 89.5 to 93.5 | |
| 0 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 3.8 to 4.5 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 14.5 to 16.5 |
| Nitrogen (N), % | 0 | |
| 0.15 to 0.21 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Unspecified Rare Earths, % | 2.4 to 4.4 | |
| 0 |
| Yttrium (Y), % | 3.7 to 4.3 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |