MakeItFrom.com
Menu (ESC)

WE43B Magnesium vs. EN 1.4362 Stainless Steel

WE43B magnesium belongs to the magnesium alloys classification, while EN 1.4362 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is WE43B magnesium and the bottom bar is EN 1.4362 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
200
Elongation at Break, % 2.2
25
Fatigue Strength, MPa 110
320
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 17
79
Shear Strength, MPa 140
470
Tensile Strength: Ultimate (UTS), MPa 250
730
Tensile Strength: Yield (Proof), MPa 200
460

Thermal Properties

Latent Heat of Fusion, J/g 330
290
Maximum Temperature: Mechanical, °C 180
1060
Melting Completion (Liquidus), °C 640
1420
Melting Onset (Solidus), °C 550
1380
Specific Heat Capacity, J/kg-K 960
480
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 53
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 34
14
Density, g/cm3 1.9
7.7
Embodied Carbon, kg CO2/kg material 28
2.9
Embodied Energy, MJ/kg 250
41
Embodied Water, L/kg 910
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.2
160
Resilience: Unit (Modulus of Resilience), kJ/m3 430
530
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 61
25
Strength to Weight: Axial, points 36
26
Strength to Weight: Bending, points 46
23
Thermal Diffusivity, mm2/s 28
4.0
Thermal Shock Resistance, points 15
20

Alloy Composition

Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
22 to 24.5
Copper (Cu), % 0 to 0.020
0.1 to 0.6
Iron (Fe), % 0 to 0.010
65.5 to 74.3
Lithium (Li), % 0 to 0.2
0
Magnesium (Mg), % 89.8 to 93.5
0
Manganese (Mn), % 0 to 0.030
0 to 2.0
Molybdenum (Mo), % 0
0.1 to 0.6
Nickel (Ni), % 0 to 0.0050
3.5 to 5.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Unspecified Rare Earths, % 2.4 to 4.4
0
Yttrium (Y), % 3.7 to 4.3
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0