WE43B Magnesium vs. C95300 Bronze

WE43B magnesium belongs to the magnesium alloys classification, while C95300 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is WE43B magnesium and the bottom bar is C95300 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 44
110
Elongation at Break, % 2.2
14 to 25
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
42
Tensile Strength: Ultimate (UTS), MPa 250
520 to 610
Tensile Strength: Yield (Proof), MPa 200
190 to 310

Thermal Properties

Latent Heat of Fusion, J/g 330
230
Maximum Temperature: Mechanical, °C 180
220
Melting Completion (Liquidus), °C 640
1050
Melting Onset (Solidus), °C 550
1040
Specific Heat Capacity, J/kg-K 960
440
Thermal Conductivity, W/m-K 51
63
Thermal Expansion, µm/m-K 27
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
13
Electrical Conductivity: Equal Weight (Specific), % IACS 53
14

Otherwise Unclassified Properties

Base Metal Price, % relative 34
28
Density, g/cm3 1.9
8.3
Embodied Carbon, kg CO2/kg material 28
3.1
Embodied Energy, MJ/kg 250
52
Embodied Water, L/kg 910
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.2
73 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 430
170 to 420
Stiffness to Weight: Axial, points 13
7.5
Stiffness to Weight: Bending, points 61
19
Strength to Weight: Axial, points 36
17 to 21
Strength to Weight: Bending, points 46
17 to 19
Thermal Diffusivity, mm2/s 28
17
Thermal Shock Resistance, points 15
19 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
9.0 to 11
Copper (Cu), % 0 to 0.020
86.5 to 90.2
Iron (Fe), % 0 to 0.010
0.8 to 1.5
Lithium (Li), % 0 to 0.2
0
Magnesium (Mg), % 89.8 to 93.5
0
Manganese (Mn), % 0 to 0.030
0
Nickel (Ni), % 0 to 0.0050
0
Unspecified Rare Earths, % 2.4 to 4.4
0
Yttrium (Y), % 3.7 to 4.3
0
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0.4 to 1.0
0
Residuals, % 0
0 to 1.0