Work Hardened 88-silver 12-tin-oxide vs. Work Hardened 90-platinum 10-iridium
Both work hardened 88-silver 12-tin-oxide and work hardened 90-platinum 10-iridium are otherwise unclassified metals. Both are furnished in the cold worked (strain hardened) condition. There are 3 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is work hardened 88-silver 12-tin-oxide and the bottom bar is work hardened 90-platinum 10-iridium.
Metric UnitsUS Customary Units
Material Properties
Elongation at Break, % | 9.0 | |
5.5 |
Shear Strength, MPa | 160 | |
320 |
Tensile Strength: Ultimate (UTS), MPa | 280 | |
550 |