Work Hardened 88-silver 12-tin-oxide vs. Work Hardened 90-silver 10-tin-oxide
Both work hardened 88-silver 12-tin-oxide and work hardened 90-silver 10-tin-oxide are otherwise unclassified metals. Both are furnished in the cold worked (strain hardened) condition.
For each property being compared, the top bar is work hardened 88-silver 12-tin-oxide and the bottom bar is work hardened 90-silver 10-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 | |
| 77 |
| Elongation at Break, % | 9.0 | |
| 7.0 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 | |
| 20 |
| Shear Strength, MPa | 160 | |
| 170 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 300 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 280 |