ZC63A Magnesium vs. EN 1.3967 Stainless Steel

ZC63A magnesium belongs to the magnesium alloys classification, while EN 1.3967 stainless steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZC63A magnesium and the bottom bar is EN 1.3967 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 60
200
Elastic (Young's, Tensile) Modulus, GPa 48
200
Elongation at Break, % 3.3
22
Fatigue Strength, MPa 94
240
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 19
79
Tensile Strength: Ultimate (UTS), MPa 220
690
Tensile Strength: Yield (Proof), MPa 130
350

Thermal Properties

Latent Heat of Fusion, J/g 330
300
Maximum Temperature: Mechanical, °C 98
1070
Melting Completion (Liquidus), °C 550
1430
Melting Onset (Solidus), °C 470
1380
Specific Heat Capacity, J/kg-K 950
470
Thermal Expansion, µm/m-K 26
16

Otherwise Unclassified Properties

Base Metal Price, % relative 13
25
Density, g/cm3 2.1
7.9
Embodied Carbon, kg CO2/kg material 22
4.8
Embodied Energy, MJ/kg 150
66
Embodied Water, L/kg 920
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.3
130
Resilience: Unit (Modulus of Resilience), kJ/m3 190
310
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 58
25
Strength to Weight: Axial, points 29
24
Strength to Weight: Bending, points 38
22
Thermal Shock Resistance, points 12
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
20 to 21.5
Copper (Cu), % 2.4 to 3.0
0
Iron (Fe), % 0
50.3 to 57.8
Magnesium (Mg), % 89.2 to 91.9
0
Manganese (Mn), % 0.25 to 0.75
4.0 to 6.0
Molybdenum (Mo), % 0
3.0 to 3.5
Nickel (Ni), % 0 to 0.010
15 to 17
Niobium (Nb), % 0
0 to 0.25
Nitrogen (N), % 0
0.2 to 0.35
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.2
0 to 1.0
Sulfur (S), % 0
0 to 0.010
Zinc (Zn), % 5.5 to 6.5
0
Residuals, % 0 to 0.3
0