ZC63A Magnesium vs. EN 1.4112 Stainless Steel

ZC63A magnesium belongs to the magnesium alloys classification, while EN 1.4112 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZC63A magnesium and the bottom bar is EN 1.4112 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 60
230
Elastic (Young's, Tensile) Modulus, GPa 48
200
Elongation at Break, % 3.3
20
Fatigue Strength, MPa 94
280
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 19
77
Shear Strength, MPa 130
470
Tensile Strength: Ultimate (UTS), MPa 220
750
Tensile Strength: Yield (Proof), MPa 130
430

Thermal Properties

Latent Heat of Fusion, J/g 330
280
Maximum Temperature: Mechanical, °C 98
910
Melting Completion (Liquidus), °C 550
1430
Melting Onset (Solidus), °C 470
1390
Specific Heat Capacity, J/kg-K 950
480
Thermal Conductivity, W/m-K 120
15
Thermal Expansion, µm/m-K 26
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 140
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
10
Density, g/cm3 2.1
7.7
Embodied Carbon, kg CO2/kg material 22
2.6
Embodied Energy, MJ/kg 150
37
Embodied Water, L/kg 920
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.3
130
Resilience: Unit (Modulus of Resilience), kJ/m3 190
480
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 58
25
Strength to Weight: Axial, points 29
27
Strength to Weight: Bending, points 38
24
Thermal Diffusivity, mm2/s 58
4.1
Thermal Shock Resistance, points 12
26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.85 to 1.0
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 2.4 to 3.0
0
Iron (Fe), % 0
76.6 to 81.2
Magnesium (Mg), % 89.2 to 91.9
0
Manganese (Mn), % 0.25 to 0.75
0 to 1.0
Molybdenum (Mo), % 0
0.9 to 1.3
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.2
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Vanadium (V), % 0
0.070 to 0.12
Zinc (Zn), % 5.5 to 6.5
0
Residuals, % 0 to 0.3
0