ZC63A Magnesium vs. EN 1.4306 Stainless Steel

ZC63A magnesium belongs to the magnesium alloys classification, while EN 1.4306 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZC63A magnesium and the bottom bar is EN 1.4306 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 60
190 to 270
Elastic (Young's, Tensile) Modulus, GPa 48
200
Elongation at Break, % 3.3
14 to 45
Fatigue Strength, MPa 94
190 to 330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 19
77
Shear Strength, MPa 130
400 to 550
Tensile Strength: Ultimate (UTS), MPa 220
580 to 900
Tensile Strength: Yield (Proof), MPa 130
210 to 570

Thermal Properties

Latent Heat of Fusion, J/g 330
290
Maximum Temperature: Mechanical, °C 98
960
Melting Completion (Liquidus), °C 550
1420
Melting Onset (Solidus), °C 470
1380
Specific Heat Capacity, J/kg-K 950
480
Thermal Conductivity, W/m-K 120
15
Thermal Expansion, µm/m-K 26
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 140
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 13
16
Density, g/cm3 2.1
7.8
Embodied Carbon, kg CO2/kg material 22
3.2
Embodied Energy, MJ/kg 150
45
Embodied Water, L/kg 920
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.3
110 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 190
110 to 820
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 58
25
Strength to Weight: Axial, points 29
21 to 32
Strength to Weight: Bending, points 38
20 to 27
Thermal Diffusivity, mm2/s 58
4.0
Thermal Shock Resistance, points 12
13 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
18 to 20
Copper (Cu), % 2.4 to 3.0
0
Iron (Fe), % 0
64.8 to 72
Magnesium (Mg), % 89.2 to 91.9
0
Manganese (Mn), % 0.25 to 0.75
0 to 2.0
Nickel (Ni), % 0 to 0.010
10 to 12
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.2
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Zinc (Zn), % 5.5 to 6.5
0
Residuals, % 0 to 0.3
0