ZC63A Magnesium vs. EN 1.5525 Steel

ZC63A magnesium belongs to the magnesium alloys classification, while EN 1.5525 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZC63A magnesium and the bottom bar is EN 1.5525 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 60
130 to 180
Elastic (Young's, Tensile) Modulus, GPa 48
190
Elongation at Break, % 3.3
11 to 21
Fatigue Strength, MPa 94
210 to 310
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 19
73
Shear Strength, MPa 130
310 to 350
Tensile Strength: Ultimate (UTS), MPa 220
440 to 1440
Tensile Strength: Yield (Proof), MPa 130
300 to 490

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Maximum Temperature: Mechanical, °C 98
400
Melting Completion (Liquidus), °C 550
1460
Melting Onset (Solidus), °C 470
1420
Specific Heat Capacity, J/kg-K 950
470
Thermal Conductivity, W/m-K 120
50
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 140
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.9
Density, g/cm3 2.1
7.8
Embodied Carbon, kg CO2/kg material 22
1.4
Embodied Energy, MJ/kg 150
19
Embodied Water, L/kg 920
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.3
44 to 240
Resilience: Unit (Modulus of Resilience), kJ/m3 190
240 to 640
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 58
24
Strength to Weight: Axial, points 29
16 to 51
Strength to Weight: Bending, points 38
16 to 36
Thermal Diffusivity, mm2/s 58
13
Thermal Shock Resistance, points 12
13 to 42

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0
0.18 to 0.23
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 2.4 to 3.0
0 to 0.25
Iron (Fe), % 0
97.7 to 98.9
Magnesium (Mg), % 89.2 to 91.9
0
Manganese (Mn), % 0.25 to 0.75
0.9 to 1.2
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.2
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Zinc (Zn), % 5.5 to 6.5
0
Residuals, % 0 to 0.3
0