ZC63A Magnesium vs. SAE-AISI L2 Steel

ZC63A magnesium belongs to the magnesium alloys classification, while SAE-AISI L2 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZC63A magnesium and the bottom bar is SAE-AISI L2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 48
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 19
72
Tensile Strength: Ultimate (UTS), MPa 220
590 to 1960

Thermal Properties

Latent Heat of Fusion, J/g 330
250
Melting Completion (Liquidus), °C 550
1450
Melting Onset (Solidus), °C 470
1410
Specific Heat Capacity, J/kg-K 950
470
Thermal Conductivity, W/m-K 120
44
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 140
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.4
Density, g/cm3 2.1
7.8
Embodied Carbon, kg CO2/kg material 22
1.9
Embodied Energy, MJ/kg 150
27
Embodied Water, L/kg 920
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 58
24
Strength to Weight: Axial, points 29
21 to 70
Strength to Weight: Bending, points 38
20 to 45
Thermal Diffusivity, mm2/s 58
12
Thermal Shock Resistance, points 12
19 to 65

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.45 to 1.0
Chromium (Cr), % 0
0.7 to 1.2
Copper (Cu), % 2.4 to 3.0
0 to 0.25
Iron (Fe), % 0
95.5 to 98.7
Magnesium (Mg), % 89.2 to 91.9
0
Manganese (Mn), % 0.25 to 0.75
0.1 to 0.9
Molybdenum (Mo), % 0
0 to 0.25
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.2
0 to 0.5
Sulfur (S), % 0
0 to 0.030
Vanadium (V), % 0
0.1 to 0.3
Zinc (Zn), % 5.5 to 6.5
0
Residuals, % 0 to 0.3
0