ZC63A magnesium belongs to the magnesium alloys classification, while C26800 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZC63A magnesium and the bottom bar is C26800 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 48
110
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 19
40
Tensile Strength: Ultimate (UTS), MPa 220
310 to 650

Thermal Properties

Latent Heat of Fusion, J/g 330
180
Maximum Temperature: Mechanical, °C 98
130
Melting Completion (Liquidus), °C 550
930
Melting Onset (Solidus), °C 470
900
Specific Heat Capacity, J/kg-K 950
390
Thermal Conductivity, W/m-K 120
120
Thermal Expansion, µm/m-K 26
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 32
27
Electrical Conductivity: Equal Weight (Specific), % IACS 140
30

Otherwise Unclassified Properties

Base Metal Price, % relative 13
24
Density, g/cm3 2.1
8.1
Embodied Carbon, kg CO2/kg material 22
2.7
Embodied Energy, MJ/kg 150
45
Embodied Water, L/kg 920
320

Common Calculations

Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 58
19
Strength to Weight: Axial, points 29
11 to 22
Strength to Weight: Bending, points 38
13 to 21
Thermal Diffusivity, mm2/s 58
37
Thermal Shock Resistance, points 12
10 to 22

Alloy Composition

Copper (Cu), % 2.4 to 3.0
64 to 68.5
Iron (Fe), % 0
0 to 0.050
Lead (Pb), % 0
0 to 0.15
Magnesium (Mg), % 89.2 to 91.9
0
Manganese (Mn), % 0.25 to 0.75
0
Nickel (Ni), % 0 to 0.010
0
Silicon (Si), % 0 to 0.2
0
Zinc (Zn), % 5.5 to 6.5
31 to 36
Residuals, % 0 to 0.3
0 to 0.3