ZK40A Magnesium vs. ACI-ASTM CD4MCuN Steel

ZK40A magnesium belongs to the magnesium alloys classification, while ACI-ASTM CD4MCuN steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZK40A magnesium and the bottom bar is ACI-ASTM CD4MCuN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 4.2
18
Fatigue Strength, MPa 190
340
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 17
79
Tensile Strength: Ultimate (UTS), MPa 280
770
Tensile Strength: Yield (Proof), MPa 260
550

Thermal Properties

Latent Heat of Fusion, J/g 340
300
Maximum Temperature: Mechanical, °C 120
1100
Melting Completion (Liquidus), °C 600
1420
Melting Onset (Solidus), °C 540
1380
Specific Heat Capacity, J/kg-K 970
480
Thermal Conductivity, W/m-K 110
17
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 130
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
18
Density, g/cm3 1.8
7.8
Embodied Carbon, kg CO2/kg material 24
3.5
Embodied Energy, MJ/kg 160
49
Embodied Water, L/kg 950
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 12
130
Resilience: Unit (Modulus of Resilience), kJ/m3 740
760
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 65
25
Strength to Weight: Axial, points 43
28
Strength to Weight: Bending, points 53
24
Thermal Diffusivity, mm2/s 62
4.5
Thermal Shock Resistance, points 17
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
24.5 to 26.5
Copper (Cu), % 0
2.7 to 3.3
Iron (Fe), % 0
59.5 to 66.3
Magnesium (Mg), % 94.2 to 96.1
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
1.7 to 2.3
Nickel (Ni), % 0
4.7 to 6.0
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.040
Zinc (Zn), % 3.5 to 4.5
0
Zirconium (Zr), % 0.45 to 1.0
0
Residuals, % 0 to 0.3
0