ZK40A Magnesium vs. SAE-AISI 1035 Steel

ZK40A magnesium belongs to the magnesium alloys classification, while SAE-AISI 1035 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZK40A magnesium and the bottom bar is SAE-AISI 1035 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 4.2
13 to 21
Fatigue Strength, MPa 190
210 to 340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
73
Shear Strength, MPa 160
360 to 370
Tensile Strength: Ultimate (UTS), MPa 280
570 to 620
Tensile Strength: Yield (Proof), MPa 260
300 to 530

Thermal Properties

Latent Heat of Fusion, J/g 340
250
Maximum Temperature: Mechanical, °C 120
400
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 540
1420
Specific Heat Capacity, J/kg-K 970
470
Thermal Conductivity, W/m-K 110
51
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 130
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.8
Density, g/cm3 1.8
7.8
Embodied Carbon, kg CO2/kg material 24
1.4
Embodied Energy, MJ/kg 160
18
Embodied Water, L/kg 950
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 12
79 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 740
250 to 740
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 65
24
Strength to Weight: Axial, points 43
20 to 22
Strength to Weight: Bending, points 53
19 to 21
Thermal Diffusivity, mm2/s 62
14
Thermal Shock Resistance, points 17
18 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.32 to 0.38
Iron (Fe), % 0
98.6 to 99.08
Magnesium (Mg), % 94.2 to 96.1
0
Manganese (Mn), % 0
0.6 to 0.9
Phosphorus (P), % 0
0 to 0.040
Sulfur (S), % 0
0 to 0.050
Zinc (Zn), % 3.5 to 4.5
0
Zirconium (Zr), % 0.45 to 1.0
0
Residuals, % 0 to 0.3
0