ZK40A magnesium belongs to the magnesium alloys classification, while C34200 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZK40A magnesium and the bottom bar is C34200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
100
Elongation at Break, % 4.2
3.0 to 17
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 17
40
Shear Strength, MPa 160
230 to 360
Tensile Strength: Ultimate (UTS), MPa 280
370 to 650
Tensile Strength: Yield (Proof), MPa 260
150 to 420

Thermal Properties

Latent Heat of Fusion, J/g 340
170
Maximum Temperature: Mechanical, °C 120
120
Melting Completion (Liquidus), °C 600
910
Melting Onset (Solidus), °C 540
890
Specific Heat Capacity, J/kg-K 970
380
Thermal Conductivity, W/m-K 110
120
Thermal Expansion, µm/m-K 26
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
26
Electrical Conductivity: Equal Weight (Specific), % IACS 130
29

Otherwise Unclassified Properties

Base Metal Price, % relative 13
24
Density, g/cm3 1.8
8.2
Embodied Carbon, kg CO2/kg material 24
2.6
Embodied Energy, MJ/kg 160
45
Embodied Water, L/kg 950
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 12
9.0 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 740
110 to 870
Stiffness to Weight: Axial, points 14
7.1
Stiffness to Weight: Bending, points 65
19
Strength to Weight: Axial, points 43
13 to 22
Strength to Weight: Bending, points 53
14 to 20
Thermal Diffusivity, mm2/s 62
37
Thermal Shock Resistance, points 17
12 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 0
62 to 65
Iron (Fe), % 0
0 to 0.1
Lead (Pb), % 0
1.5 to 2.5
Magnesium (Mg), % 94.2 to 96.1
0
Zinc (Zn), % 3.5 to 4.5
32 to 36.5
Zirconium (Zr), % 0.45 to 1.0
0
Residuals, % 0 to 0.3
0 to 0.4