Zamak 2 vs. AWS BAg-20

Zamak 2 belongs to the zinc alloys classification, while AWS BAg-20 belongs to the otherwise unclassified metals. They have a modest 35% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is Zamak 2 and the bottom bar is AWS BAg-20.

Zamak 2 (ASTM AC43A, Z35541, Mazak 2) Zinc Alloy AWS BAg-20 (P07301) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		87
Elastic (Young's, Tensile) Modulus, GPa		93

Poisson's Ratio		0.26
Poisson's Ratio		0.32

Shear Modulus, GPa		33
Shear Modulus, GPa		35

Tensile Strength: Ultimate (UTS), MPa		360
Tensile Strength: Ultimate (UTS), MPa		160

Thermal Properties

Latent Heat of Fusion, J/g		130
Latent Heat of Fusion, J/g		150

Melting Completion (Liquidus), °C		390
Melting Completion (Liquidus), °C		770

Melting Onset (Solidus), °C		380
Melting Onset (Solidus), °C		680

Specific Heat Capacity, J/kg-K		410
Specific Heat Capacity, J/kg-K		340

Thermal Expansion, µm/m-K		28
Thermal Expansion, µm/m-K		21

Otherwise Unclassified Properties

Density, g/cm³		6.5
Density, g/cm³		8.6

Embodied Carbon, kg CO₂/kg material		3.0
Embodied Carbon, kg CO₂/kg material		30

Embodied Energy, MJ/kg		57
Embodied Energy, MJ/kg		480

Common Calculations

Stiffness to Weight: Axial, points		7.5
Stiffness to Weight: Axial, points		6.0

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		17

Strength to Weight: Axial, points		15
Strength to Weight: Axial, points		5.1

Strength to Weight: Bending, points		17
Strength to Weight: Bending, points		7.6

Thermal Shock Resistance, points		11
Thermal Shock Resistance, points		5.9

Alloy Composition

Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460

Aluminum (Al), %		3.5 to 4.3
Aluminum (Al), %		0

Cadmium (Cd), %		0 to 0.0050
Cadmium (Cd), %		0

Copper (Cu), %		2.5 to 3.3
Copper (Cu), %		37 to 39

Iron (Fe), %		0 to 0.1
Iron (Fe), %		0

Lead (Pb), %		0 to 0.0050
Lead (Pb), %		0

Magnesium (Mg), %		0.020 to 0.060
Magnesium (Mg), %		0

Nickel (Ni), %		0 to 0.020
Nickel (Ni), %		0

Silicon (Si), %		0 to 0.030
Silicon (Si), %		0

Silver (Ag), %		0
Silver (Ag), %		29 to 31

Tin (Sn), %		0 to 0.0030
Tin (Sn), %		0

Zinc (Zn), %		92.2 to 94
Zinc (Zn), %		30 to 34

Residuals, %		0
Residuals, %		0 to 0.15