Zamak 3 vs. EN 1.1061 Steel

Zamak 3 belongs to the zinc alloys classification, while EN 1.1061 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is Zamak 3 and the bottom bar is EN 1.1061 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 83
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 86
190
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 33
72
Tensile Strength: Ultimate (UTS), MPa 280
530 to 1810

Thermal Properties

Latent Heat of Fusion, J/g 120
250
Maximum Temperature: Mechanical, °C 95
400
Melting Completion (Liquidus), °C 390
1460
Melting Onset (Solidus), °C 380
1420
Specific Heat Capacity, J/kg-K 410
470
Thermal Conductivity, W/m-K 110
51
Thermal Expansion, µm/m-K 27
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 38
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 11
1.8
Density, g/cm3 6.4
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 57
19
Embodied Water, L/kg 380
46

Common Calculations

Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 12
19 to 64
Strength to Weight: Bending, points 15
19 to 42
Thermal Diffusivity, mm2/s 43
14
Thermal Shock Resistance, points 8.6
17 to 58

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.42 to 0.5
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 0 to 0.1
98.1 to 99.06
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.020 to 0.060
0
Manganese (Mn), % 0
0.5 to 0.8
Nickel (Ni), % 0 to 0.020
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.030
0 to 0.3
Sulfur (S), % 0
0.020 to 0.035
Tin (Sn), % 0 to 0.0030
0
Zinc (Zn), % 95.3 to 96.5
0