MakeItFrom.com
Menu (ESC)

Zamak 5 vs. AWS BAg-13

Zamak 5 belongs to the zinc alloys classification, while AWS BAg-13 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is AWS BAg-13.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
91
Poisson's Ratio 0.25
0.35
Shear Modulus, GPa 33
34
Tensile Strength: Ultimate (UTS), MPa 330
180

Thermal Properties

Latent Heat of Fusion, J/g 120
150
Melting Completion (Liquidus), °C 390
860
Melting Onset (Solidus), °C 380
720
Specific Heat Capacity, J/kg-K 410
310
Thermal Expansion, µm/m-K 27
19

Otherwise Unclassified Properties

Density, g/cm3 6.4
9.7
Embodied Carbon, kg CO2/kg material 3.0
52
Embodied Energy, MJ/kg 57
820

Common Calculations

Stiffness to Weight: Axial, points 7.5
5.2
Stiffness to Weight: Bending, points 23
16
Strength to Weight: Axial, points 14
5.2
Strength to Weight: Bending, points 16
7.3
Thermal Shock Resistance, points 9.9
7.5

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 3.5 to 4.3
0
Cadmium (Cd), % 0 to 0.0050
0
Copper (Cu), % 0.7 to 1.3
37.4 to 42.5
Iron (Fe), % 0 to 0.1
0
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Nickel (Ni), % 0 to 0.020
0.5 to 1.5
Silicon (Si), % 0 to 0.030
0
Silver (Ag), % 0
53 to 55
Tin (Sn), % 0 to 0.0030
0
Zinc (Zn), % 94.3 to 95.7
4.0 to 6.0
Residuals, % 0
0 to 0.15