Zamak 5 vs. EN 1.0501 Steel

Zamak 5 belongs to the zinc alloys classification, while EN 1.0501 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is EN 1.0501 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92
160
Elastic (Young's, Tensile) Modulus, GPa 87
190
Elongation at Break, % 6.3
19
Fatigue Strength, MPa 56
190
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 33
73
Shear Strength, MPa 260
350
Tensile Strength: Ultimate (UTS), MPa 330
560
Tensile Strength: Yield (Proof), MPa 240
280

Thermal Properties

Latent Heat of Fusion, J/g 120
250
Maximum Temperature: Mechanical, °C 95
400
Melting Completion (Liquidus), °C 390
1460
Melting Onset (Solidus), °C 380
1420
Specific Heat Capacity, J/kg-K 410
470
Thermal Conductivity, W/m-K 110
48
Thermal Expansion, µm/m-K 27
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.1
Density, g/cm3 6.4
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 57
19
Embodied Water, L/kg 380
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19
90
Resilience: Unit (Modulus of Resilience), kJ/m3 330
210
Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 14
20
Strength to Weight: Bending, points 16
19
Thermal Diffusivity, mm2/s 42
13
Thermal Shock Resistance, points 9.9
18

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.32 to 0.39
Chromium (Cr), % 0
0 to 0.4
Copper (Cu), % 0.7 to 1.3
0
Iron (Fe), % 0 to 0.1
97.4 to 99.18
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Manganese (Mn), % 0
0.5 to 0.8
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0 to 0.020
0 to 0.4
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.030
0 to 0.4
Sulfur (S), % 0
0 to 0.045
Tin (Sn), % 0 to 0.0030
0
Zinc (Zn), % 94.3 to 95.7
0