Zamak 5 vs. EN 1.4105 Stainless Steel

Zamak 5 belongs to the zinc alloys classification, while EN 1.4105 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is EN 1.4105 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92
180
Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 6.3
23
Fatigue Strength, MPa 56
190
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 33
77
Shear Strength, MPa 260
340
Tensile Strength: Ultimate (UTS), MPa 330
530
Tensile Strength: Yield (Proof), MPa 240
290

Thermal Properties

Latent Heat of Fusion, J/g 120
290
Maximum Temperature: Mechanical, °C 95
870
Melting Completion (Liquidus), °C 390
1430
Melting Onset (Solidus), °C 380
1390
Specific Heat Capacity, J/kg-K 410
480
Thermal Conductivity, W/m-K 110
25
Thermal Expansion, µm/m-K 27
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 37
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
9.0
Density, g/cm3 6.4
7.7
Embodied Carbon, kg CO2/kg material 3.0
2.2
Embodied Energy, MJ/kg 57
31
Embodied Water, L/kg 380
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19
100
Resilience: Unit (Modulus of Resilience), kJ/m3 330
210
Stiffness to Weight: Axial, points 7.5
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 14
19
Strength to Weight: Bending, points 16
19
Thermal Diffusivity, mm2/s 42
6.7
Thermal Shock Resistance, points 9.9
19

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.080
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 0.7 to 1.3
0
Iron (Fe), % 0 to 0.1
77.9 to 83.7
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Manganese (Mn), % 0
0 to 1.5
Molybdenum (Mo), % 0
0.2 to 0.6
Nickel (Ni), % 0 to 0.020
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.030
0 to 1.5
Sulfur (S), % 0
0.15 to 0.35
Tin (Sn), % 0 to 0.0030
0
Zinc (Zn), % 94.3 to 95.7
0