Zamak 5 vs. EN 1.7077 Steel

Zamak 5 belongs to the zinc alloys classification, while EN 1.7077 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is EN 1.7077 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 87
190
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 33
73
Tensile Strength: Ultimate (UTS), MPa 330
490 to 1750

Thermal Properties

Latent Heat of Fusion, J/g 120
250
Maximum Temperature: Mechanical, °C 95
420
Melting Completion (Liquidus), °C 390
1460
Melting Onset (Solidus), °C 380
1420
Specific Heat Capacity, J/kg-K 410
470
Thermal Conductivity, W/m-K 110
45
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.3
Density, g/cm3 6.4
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 57
19
Embodied Water, L/kg 380
51

Common Calculations

Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 14
17 to 62
Strength to Weight: Bending, points 16
18 to 41
Thermal Diffusivity, mm2/s 42
12
Thermal Shock Resistance, points 9.9
14 to 51

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0
Boron (B), % 0
0.00080 to 0.0050
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.34 to 0.38
Chromium (Cr), % 0
0.9 to 1.2
Copper (Cu), % 0.7 to 1.3
0 to 0.25
Iron (Fe), % 0 to 0.1
96.8 to 98.1
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Manganese (Mn), % 0
0.7 to 1.0
Nickel (Ni), % 0 to 0.020
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.030
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Tin (Sn), % 0 to 0.0030
0
Zinc (Zn), % 94.3 to 95.7
0