Zamak 5 vs. EN 1.7239 Steel

Zamak 5 belongs to the zinc alloys classification, while EN 1.7239 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is EN 1.7239 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92
200 to 480
Elastic (Young's, Tensile) Modulus, GPa 87
190
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 33
73
Tensile Strength: Ultimate (UTS), MPa 330
660 to 1990

Thermal Properties

Latent Heat of Fusion, J/g 120
250
Maximum Temperature: Mechanical, °C 95
420
Melting Completion (Liquidus), °C 390
1460
Melting Onset (Solidus), °C 380
1410
Specific Heat Capacity, J/kg-K 410
470
Thermal Conductivity, W/m-K 110
44
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.3
Density, g/cm3 6.4
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.5
Embodied Energy, MJ/kg 57
20
Embodied Water, L/kg 380
50

Common Calculations

Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 14
23 to 71
Strength to Weight: Bending, points 16
21 to 45
Thermal Diffusivity, mm2/s 42
12
Thermal Shock Resistance, points 9.9
19 to 59

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.56 to 0.64
Chromium (Cr), % 0
0.7 to 1.0
Copper (Cu), % 0.7 to 1.3
0
Iron (Fe), % 0 to 0.1
96.8 to 98
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Manganese (Mn), % 0
0.7 to 1.0
Molybdenum (Mo), % 0
0.060 to 0.15
Nickel (Ni), % 0 to 0.020
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.030
0 to 0.4
Sulfur (S), % 0
0 to 0.025
Tin (Sn), % 0 to 0.0030
0
Zinc (Zn), % 94.3 to 95.7
0