Zamak 5 vs. EN 1.8891 Steel

Zamak 5 belongs to the zinc alloys classification, while EN 1.8891 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is EN 1.8891 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92
180
Elastic (Young's, Tensile) Modulus, GPa 87
190
Elongation at Break, % 6.3
19
Fatigue Strength, MPa 56
330
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 33
73
Shear Strength, MPa 260
380
Tensile Strength: Ultimate (UTS), MPa 330
610
Tensile Strength: Yield (Proof), MPa 240
480

Thermal Properties

Latent Heat of Fusion, J/g 120
250
Maximum Temperature: Mechanical, °C 95
400
Melting Completion (Liquidus), °C 390
1460
Melting Onset (Solidus), °C 380
1420
Specific Heat Capacity, J/kg-K 410
470
Thermal Conductivity, W/m-K 110
46
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.5
Density, g/cm3 6.4
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.7
Embodied Energy, MJ/kg 57
24
Embodied Water, L/kg 380
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19
110
Resilience: Unit (Modulus of Resilience), kJ/m3 330
630
Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 14
22
Strength to Weight: Bending, points 16
20
Thermal Diffusivity, mm2/s 42
12
Thermal Shock Resistance, points 9.9
18

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0.020 to 0.060
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.2
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0.7 to 1.3
0 to 0.7
Iron (Fe), % 0 to 0.1
95.2 to 99
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Manganese (Mn), % 0
1.0 to 1.7
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0 to 0.020
0 to 0.8
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.025
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.030
0 to 0.6
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.2
Zinc (Zn), % 94.3 to 95.7
0