Zamak 5 belongs to the zinc alloys classification, while EN 1.8959 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is EN 1.8959 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92
170
Elastic (Young's, Tensile) Modulus, GPa 87
190
Elongation at Break, % 6.3
16
Fatigue Strength, MPa 56
220
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 33
73
Shear Strength, MPa 260
350
Tensile Strength: Ultimate (UTS), MPa 330
570
Tensile Strength: Yield (Proof), MPa 240
340

Thermal Properties

Latent Heat of Fusion, J/g 120
250
Maximum Temperature: Mechanical, °C 95
420
Melting Completion (Liquidus), °C 390
1460
Melting Onset (Solidus), °C 380
1420
Specific Heat Capacity, J/kg-K 410
470
Thermal Conductivity, W/m-K 110
39
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.7
Density, g/cm3 6.4
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.6
Embodied Energy, MJ/kg 57
21
Embodied Water, L/kg 380
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19
78
Resilience: Unit (Modulus of Resilience), kJ/m3 330
300
Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 14
20
Strength to Weight: Bending, points 16
19
Thermal Diffusivity, mm2/s 42
10
Thermal Shock Resistance, points 9.9
17

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.19
Chromium (Cr), % 0
0.35 to 0.85
Copper (Cu), % 0.7 to 1.3
0.2 to 0.6
Iron (Fe), % 0 to 0.1
94.9 to 99
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Manganese (Mn), % 0
0.45 to 1.6
Molybdenum (Mo), % 0
0 to 0.35
Nickel (Ni), % 0 to 0.020
0 to 0.7
Nitrogen (N), % 0
0 to 0.010
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.030
0 to 0.55
Sulfur (S), % 0
0 to 0.040
Tin (Sn), % 0 to 0.0030
0
Zinc (Zn), % 94.3 to 95.7
0
Zirconium (Zr), % 0
0 to 0.17