Zamak 5 vs. SAE-AISI 1527 Steel

Zamak 5 belongs to the zinc alloys classification, while SAE-AISI 1527 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is SAE-AISI 1527 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92
170 to 180
Elastic (Young's, Tensile) Modulus, GPa 87
190
Elongation at Break, % 6.3
13 to 21
Fatigue Strength, MPa 56
220 to 350
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 33
73
Shear Strength, MPa 260
370 to 390
Tensile Strength: Ultimate (UTS), MPa 330
590 to 640
Tensile Strength: Yield (Proof), MPa 240
320 to 550

Thermal Properties

Latent Heat of Fusion, J/g 120
250
Maximum Temperature: Mechanical, °C 95
400
Melting Completion (Liquidus), °C 390
1460
Melting Onset (Solidus), °C 380
1420
Specific Heat Capacity, J/kg-K 410
470
Thermal Conductivity, W/m-K 110
52
Thermal Expansion, µm/m-K 27
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 12
1.8
Density, g/cm3 6.4
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 57
19
Embodied Water, L/kg 380
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19
82 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 330
260 to 800
Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 14
21 to 23
Strength to Weight: Bending, points 16
20 to 21
Thermal Diffusivity, mm2/s 42
14
Thermal Shock Resistance, points 9.9
19 to 20

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.22 to 0.29
Copper (Cu), % 0.7 to 1.3
0
Iron (Fe), % 0 to 0.1
98.1 to 98.6
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Manganese (Mn), % 0
1.2 to 1.5
Nickel (Ni), % 0 to 0.020
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.030
0
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0 to 0.0030
0
Zinc (Zn), % 94.3 to 95.7
0