Zamak 5 vs. SAE-AISI H43 Steel

Zamak 5 belongs to the zinc alloys classification, while SAE-AISI H43 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is SAE-AISI H43 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
200
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 33
77
Tensile Strength: Ultimate (UTS), MPa 330
710 to 2140

Thermal Properties

Latent Heat of Fusion, J/g 120
270
Melting Completion (Liquidus), °C 390
1530
Melting Onset (Solidus), °C 380
1480
Specific Heat Capacity, J/kg-K 410
460
Thermal Conductivity, W/m-K 110
30
Thermal Expansion, µm/m-K 27
12

Otherwise Unclassified Properties

Base Metal Price, % relative 12
14
Density, g/cm3 6.4
7.9
Embodied Carbon, kg CO2/kg material 3.0
8.2
Embodied Energy, MJ/kg 57
120
Embodied Water, L/kg 380
100

Common Calculations

Stiffness to Weight: Axial, points 7.5
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 14
25 to 75
Strength to Weight: Bending, points 16
22 to 46
Thermal Diffusivity, mm2/s 42
8.3
Thermal Shock Resistance, points 9.9
21 to 62

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.5 to 0.65
Chromium (Cr), % 0
3.8 to 4.5
Copper (Cu), % 0.7 to 1.3
0
Iron (Fe), % 0 to 0.1
83.2 to 85.9
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Manganese (Mn), % 0
0.15 to 0.4
Molybdenum (Mo), % 0
7.8 to 8.5
Nickel (Ni), % 0 to 0.020
0
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.030
0.2 to 0.45
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.0030
0
Vanadium (V), % 0
1.8 to 2.2
Zinc (Zn), % 94.3 to 95.7
0