Zamak 5 vs. SAE-AISI S1 Steel

Zamak 5 belongs to the zinc alloys classification, while SAE-AISI S1 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is SAE-AISI S1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
190
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 33
73
Tensile Strength: Ultimate (UTS), MPa 330
690 to 1840

Thermal Properties

Latent Heat of Fusion, J/g 120
260
Melting Completion (Liquidus), °C 390
1500
Melting Onset (Solidus), °C 380
1450
Specific Heat Capacity, J/kg-K 410
470
Thermal Conductivity, W/m-K 110
41
Thermal Expansion, µm/m-K 27
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
8.0
Density, g/cm3 6.4
8.0
Embodied Carbon, kg CO2/kg material 3.0
2.6
Embodied Energy, MJ/kg 57
37
Embodied Water, L/kg 380
56

Common Calculations

Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 14
24 to 64
Strength to Weight: Bending, points 16
22 to 42
Thermal Diffusivity, mm2/s 42
11
Thermal Shock Resistance, points 9.9
21 to 56

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.4 to 0.55
Chromium (Cr), % 0
1.0 to 1.8
Copper (Cu), % 0.7 to 1.3
0 to 0.25
Iron (Fe), % 0 to 0.1
91.6 to 96.7
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Manganese (Mn), % 0
0.1 to 0.4
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0 to 0.020
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.030
0.15 to 1.2
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.0030
0
Tungsten (W), % 0
1.5 to 3.0
Vanadium (V), % 0
0.15 to 0.3
Zinc (Zn), % 94.3 to 95.7
0